国际硅铁标准（ISO 5445-80） 表1、硅铁牌号和化学成分
| 牌号 |
化学成分，% |
|||||||||
| Si |
Al |
P |
S |
C |
Mn |
Cr |
Ti |
|||
| > |
≤ |
> |
≤ |
≤ |
||||||
| FeSi10 |
8.0 |
13.0 |
0.2 |
0.15 |
0.06 |
2.0 |
3.0 |
0.8 |
0.3 |
|
| FeSi15 |
14.0 |
13.0 |
1.0 |
0.15 |
0.06 |
1.5 |
1.5 |
0.8 |
0.3 |
|
| FeSi25 |
20.0 |
20.0 |
1.5 |
0.15 |
0.06 |
1.0 |
1.0 |
0.8 |
0.3 |
|
| FeSi45 |
41.0 |
30.0 |
2.0 |
0.05 |
0.05 |
0.2 |
1.0 |
0.5 |
0.3 |
|
| FeSi50 |
47.0 |
47.0 |
1.5 |
0.05 |
0.05 |
0.2 |
0.8 |
0.5 |
0.3 |
|
| FeSi65 |
63.0 |
51.0 |
2.0 |
0.05 |
0.04 |
0.2 |
0.4 |
0.4 |
0.3 |
|
| FeSi75Al |
72.0 |
68.0 |
1.0 |
0.05 |
0.04 |
0.15 |
0.5 |
0.3 |
0.3 |
|
| FeSi75Al1.5 |
72.0 |
80.0 |
1.0 |
1.5 |
0.05 |
0.04 |
0.15 |
0.5 |
0.3 |
0.3 |
| FeSi75Al2 |
72.0 |
80.0 |
1.5 |
2.0 |
0.05 |
0.04 |
0.2 |
0.5 |
0.3 |
0.3 |
| FeSi75Al3 |
72.0 |
80.0 |
2.0 |
3.0 |
0.05 |
0.04 |
0.2 |
0.5 |
0.5 |
0.3 |
| FeSi90Al1 |
87.0 |
95.0 |
1.5 |
0.04 |
0.04 |
0.15 |
0.5 |
0.2 |
0.3 |
|
| FeSi90Al2 |
87.0 |
95.0 |
1.5 |
3.0 |
0.04 |
0.04 |
0.15 |
0.5 |
0.2 |
0.3 |
注：如无另外规定，则这些数值仅为资料列出。 表2、硅铁的颗粒粒度
| 等级 |
粒度范围/"left" width="134"> 过细粒度（最大）% |
过粗粒度（最大）/% |
||
| 总量 |
<3.15"left" width="134"> |
|||
| 1 |
100-315 |
20 |
6 |
10（在两个或3个方向上，不得有超过规定粒度范围最大极限值×1.15的粒度） |
| 2 |
75-200 |
20 |
6 |
|
| 3 |
35-100 |
18 |
6 |
|
| 4 |
10-75 |
18 |
7 |
|
| 5 |
3.15-35 |
8 |
8 |
|
| 6 |
3.15-10 |
10 |
10 |
|
| 7 |
3.15-6．3 |
10 |
10 |
|
| 8 |
3.15 |
注：按组批的产品，各炉之间含硅量相差不得超过3%(绝对值)。