种类的记号 | 调质记号 | 冷轧、固溶化热处理或退火状态 | 析出硬化热处理状态 | 导电% | ||||||
硬度HV | 屈服强度N/mm | 抗拉强度N/mm | 伸长% | 热处理记号 | 硬度HV | 屈服强度N/mm | 抗拉强度N/mm | |||
301-CSP | 1/2H | 340±30 | ≥510 | ≥930 | ≥10 | - | - | - | - | 2.3 |
3/4H | 400±30 | ≥745 | ≥1130 | ≥5 | - | - | - | - | 2.3 | |
H | 460±30 | ≥1030 | ≥1320 | - | - | - | - | - | 2.3 | |
EH | 510±20 | ≥1275 | ≥1570 | - | - | - | - | - | 2.3 | |
SEH | ≥530 | ≥1450 | ≥1740 | - | - | - | - | - | 2.3 | |
304-CSP | 1/2H | 280±30 | ≥470 | ≥780 | ≥6 | - | - | - | - | 2.3 |
3/4H | 340±30 | ≥665 | ≥930 | ≥3 | - | - | - | - | 2.3 | |
H | ≥370 | ≥880 | ≥1130 | - | - | - | - | - | 2.3 | |
631-CSP | 0 | ≤200 | - | ≤1030 | ≥20 | TH1050RH950 | ≥345≥392 | ≥960≥1030 | ≥1140≥1230 | 2.3 |
1/2H | 375±25 | - | ≥1080 | ≥5 | CH | ≥380 | ≥880 | ≥1230 | 2.3 | |
3/4H | 425±25 | - | ≥1180 | CH | ≥450 | ≥1080 | ≥1420 | 2.3 | ||
H | ≥450 | - | ≥1420 | CH | ≥530 | ≥1320 | ≥1720 | 2.3 |
1.屈服强度(σ0.2):使产生永久残余塑性变形等于一定值(一般为原长度的0.2%)时的应力,称为屈服强度σ0.2。
2.抗拉强度(σb):材料在拉伸过程中,从开始到发生断裂时所达到的最大应力值。它表示钢材抵抗断裂的能力大小。设Pb为材料被拉断前达到的最大拉力,Fo为试样截面面积,则抗拉强度σb= Pb/Fo (MPa)。
3.伸长率(δs):材料在拉断后,其塑性伸长的长度与原试样长度的百分比叫伸长率或延伸率。
4.硬度:硬度表示材料抵抗硬物体压入其表面的能力。它是金属材料的重要性能指标之一。一般硬度越高,耐磨性越好。