船板力学性能与化学成分
一般强度船体结构钢力学性能与化学成份
| 钢材级别 |
屈服点 σs(MPa)不小于 |
抗拉强度 σb(MPa) |
伸长率σ% 不小于 |
碳 C |
锰 Mn |
硅 Si |
硫 S |
磷 P |
| A |
235 |
400-520 |
22 |
≤0.21 |
≥2.5C |
≤0.5 |
≤0.035 |
≤0.035 |
| B |
≤0.21 |
≥0.80 |
≤0.35 |
|||||
| D |
≤0.21 |
≥0.60 |
≤0.35 |
|||||
| E |
≤0.18 |
≥0.70 |
≤0.35 |
高强度船体结构钢力学性能与化学成份
| 钢材级别 |
屈服点σs (MPa)不小于 |
抗拉强度 σb(MPa) |
伸长率σ% 不小于 |
碳 C |
锰 Mn |
硅 Si |
硫 S |
磷 P |
| A32 |
315 |
440-570 |
22 |
≤0.18 |
≥0.9-1.60 |
≤0.50 |
≤0.035 |
≤0.035 |
| D32 |
||||||||
| E32 |
||||||||
| F32 |
≤0.16 |
≤0.025 |
≤0.025 |
|||||
| A36 |
355 |
490-630 |
21 |
≤0.18 |
≤0.035 |
≤0.035 |
||
| D36 |
||||||||
| E36 |
||||||||
| F36 |
≤0.16 |
≤0.025 |
≤0.025 |
|||||
| A40 |
390 |
510-660 |
20 |
≤0.18 |
≤0.035 |
≤0.035 |
||
| D40 |
||||||||
| E40 |
||||||||
| F40 |
≤0.16 |
≤0.025 |
≤0.025 |