MEASUREMENT测试项目

TEST METHOD 测试方法

VALUE 数值

90-minute UV post-cure 90分钟紫外固化

Hardness 硬度， Shore D

ASTM D 2240

85

Flexural modulus 弯曲模量， Mpa

ASTM D 790

2,420-2,520

Flexural strength 弯曲强度， Mpa

ASTM D 790

83- 90

Tensile modulus 拉伸模量， MPa

ASTM D 638

2,400-2,500

Tensile strength 拉伸强度， MPa

ASTM D 638

55-60

Elongation at break 断裂延长率

ASTM D 638

11 -15%

Impact strength,notched lzod, J/m缺口冲击强度

ASTM D 256

34 - 40

Heat deflection temperature, ℃热变形温度

ASTM D 648 @66PSI

70

Glass transition,Tg 玻璃化转变温度，℃

DMA，E"peak

71

Coefficient of thermal expension,热膨胀系数， /℃

TMA(T<Tg)

125*E-6

Density 密度， g/cm

1.2